Material What is T10 ?

DURA- ALLOY -- KLR60 Subdivision Description

Using qualified raw materials from reliable sources and adopting unique T1 Cooled from an elevated temperature shaping process and
refining technique, the KLR 60 is not just an alloy that similar to conventional naturally aged to a substantially stable condition.
6061.
T2 Cooled from an elevated temperature shaping process, cold
With fine-knit structure and steady quality, as a trusty and durable material, it worked, and naturally aged to a substantially stable condition.
has been constantly applied to single and double wall rim products.
T3 Solution heat-treated, cold worked, and naturally aged to a
substantially stable condition.

SUPER ALLOY -- KLM41 T4 Solution heat-treated and naturally aged to a substantially stable
condition.
Special alloy contains manganese (Mn) and niobium (Nb).
T5 Cooled from an elevated temperature shaping process and then

The melting point of niobium (Nb) is 2300°C, whereas aluminum (Al) is 620°C. artificially aged.
Due to tremendous different melting points between these elements, how to
alloying is a very difficult task in materials science. Solution heat-treated and then artificially aged.
Applies to products which are not cold worked after solution
KINLIN developed the brand-new Super Alloy--KLM41, aluminum alloy T6 heat-treatment, or in which the effect of cold work in flattening
containing niobium, by unique technology and refining technique. or straightening may not be recognized in mechanical property
limits.
Equipped tight-knit structure and fine-textured surface specialty, this alloy
offers elongation twice that of conventional alloys. This material has been T7 Solution heat-treated and overaged/stabilized.
successfully applied to the fabrication of high-end series products.
T8 Solution heat-treated, cold worked, and then artificially aged.

T9 Solution heat-treated, artificially aged, and then cold worked.

Cooled from an elevated temperature shaping process, cold
worked, and then artificially aged.
T10 Applies to products which are cold worked to improve strength,
or in which the effect of cold work in flattening or straightening is
recognized in mechanical property limits.

Source: Aluminum standards and data 1986 Metric SI, the Aluminum Association, Inc.

4 5